General Chemical Resistance

2,(2-Ethoxyethoxy)ethanol, pure - Ether, Aliphatic, Alcohol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

2,2,4-Trimethylpentane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

2,4,6-Trimethyl-1,3,5-trioxane, pure - Ketone, Aliphatic, Cyclic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

2,4-Dichlorophenol, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

2-Butanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Butanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Butoxyethanol, pure - Ether, Aliphatic, Alcohol
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

2-Butyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Butyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Ethoxyethanol, pure - Ether, Aliphatic, Alcohol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

2-Ethoxyethanol Acetate, pure - Ether, Aliphatic, Ester
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

2-Mercaptoethanol, pure - Alcohol, Aliphatic, Mercaptan
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

2-Methoxyethanol, pure - Ether, Aliphatic, Alcohol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

1,1,1-Trichloroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1,1,2-Trichloroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1,2,2,2-Tetrafluoroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1,2,4-Trichlorobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

1,2,4-Trimethylbenzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

1,2-Dichloroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

1,2-ethanediol, 30% - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

1,2-ethanediol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

1,2-propanediol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

1,3,5-Trimethylbenzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

1,3-Benzenediol, 5% - Alcohol, Aromatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

1,3-Benzenediol, saturated - Alcohol, Aromatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

1,3-Benzenediol, pure - Alcohol, Aromatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

1,3-Butanediol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1,3-Butylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1,4-benzoquinone, pure - Ketone, Aliphatic, Cyclic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1,4-Dioxane, pure - Ether, Cyclic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

1-Chlorobutane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1-Dodecanol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1-Hexadecanol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1-Nitropropane, pure - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

1-Propanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

1-Propanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

1-Propyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

1-Propyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Methoxyethanol Acetate, pure - Ether, Aliphatic, Ester
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

2-Propanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Propanol, 30% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

2-Propanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Propyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

2-Propyl Alcohol, 30% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

2-Propyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

3-Pentanone, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

4-Aminosalicylic Acid, pure - Acid, Organic, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

4-Hydroxy-4-methyl-2-pentanone, pure - Ketone, Aliphatic, Alcohol
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Acetaldehyde, 10% - Aldehyde, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Acetaldehyde, 100% - Aldehyde, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Acetaldehyde, pure - Aldehyde, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Acetamide, saturated - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetamide, unsaturated - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetamide, pure - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, <5% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 1% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 10% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 100% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 25% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 30% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 5% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 50% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 60% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, 90% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, Glacial - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Acid, pure - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Acetic Anhydride, pure - Acid, Organic, Anhydride
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Acetone, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Immediate damage may occur. Not recommended for continuous use.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Acetonitrile, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Acetophenone, pure - Ketone, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Acetylene, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Acidic Cleaning Solution - Detergent
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Acrylamide, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Acrylonitrile, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Adipic Acid, pure - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Alanine, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Alconox detergent - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Alkaline Sucrose - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Allyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Allyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Alum, 5% - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Alum, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Aluminum Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Aluminum Fluoride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Aluminum Hydroxide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Aluminum Potassium Sulfate, 5% - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Aluminum Potassium Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Aluminum Salts, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Aluminum Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Amino Acids, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonia, 25% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonia, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonia, gas, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Acetate, saturated - Salt, Organic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Acetate, pure - Salt, Organic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Carbonate, saturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Carbonate, unsaturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Carbonate, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Chloride, saturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Chloride, unsaturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Chloride, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Flouride, saturated - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Ammonium Flouride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Ammonium Fluoride, 20% - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Glycolate, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Hydroxide, 10% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 1N - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 25% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 28% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 30% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 3N - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 5% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 6% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, 6N - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, concentrated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ammonium Hydroxide, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ammonium Nitrate, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Oxalate, pure - Salt, Organic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Persulfate, saturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ammonium Persulfate, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ammonium Phosphate, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ammonium Salts, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Ammonium Sulfate, 77% - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Sulfate, saturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Sulfate, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Sulfide, saturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Sulfide, unsaturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ammonium Sulfide, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Amyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Amyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Amyl Chloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Aniline, pure - Amine, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Aqua Regia, pure - Acid, Inorganic, Oxidizer
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Arsenic Acid, pure - Acid, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Asymmetrical Trimetylbenzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Barium Salts, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Beer, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Benzaldehyde, pure - Aldehyde, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Benzenamine, pure - Amine, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Benzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Benzenesulfonic Acid, pure - Acid, Organic, Aromatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Benzoic Acid, saturated - Acid, Organic, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Benzoic Acid, pure - Acid, Organic, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Benzyl Acetate, pure - Ester, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Benzyl Alcohol, 1% - Alcohol, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Benzyl Alcohol, 100% - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Benzyl Alcohol, pure - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Benzyl Benzoate, pure - Ester, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Benzyl Carbinol, pure - Alcohol, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Benzyl Chloride, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

beta-Mercaptoethanol, pure - Alcohol, Aliphatic, Mercaptan
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Bis(2-ethylhexyl) Phthalate, pure - Ester, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Bleach - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Bleach, 5% - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Bleach, Household - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Borax, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Boric Acid, 5% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Boric Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Brine, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Bromine, pure - Element, Liquid, Oxidizer
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Bromobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Bromoform, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Butadiene, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Butane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Butanediol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Butanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Butanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Butyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Butyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Butyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Butyl Cellosolve, pure - Ether, Aliphatic, Polyol
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Butyl Chloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Butyl Phthalate, pure - Ester, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Butylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Butyraldehyde, pure - Aldehyde, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Butyric Acid, 100% - Acid, Organic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Butyric Acid, pure - Acid, Organic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Calcium Bisulfite, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Calcium Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Calcium Hydroxide, concentrated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Calcium Hypochlorite, saturated - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Calcium Hypochlorite, pure - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Calcium Salts, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Carbazole, pure - Hydrocarbon, Aromatic, Heterocyclic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Carbitol, pure - Ether, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Carbon Dioxide, pure - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Carbon Dioxide, gas, pure - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Carbon Disulfide, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Carbon Tetrachloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Carbonic Acid, pure - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Carbonic Acid, gas, pure - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Caustic Potash, 10% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Potash, 15% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Potash, 32% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Potash, 45% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Potash, 5% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Potash, 50% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Potash, concentrated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, <1% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, 1% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, 10% - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, 32% - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, 5% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, 50% - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, 52% - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Caustic Soda, concentrated - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Cedarwood Oil, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Cellosolve, pure - Ether, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Cellosolve Acetate, pure - Ether, Aliphatic, Ester
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Acetate, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Bromide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Formate, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Iodide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Trichloroacetate, pure - Salt, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cesium Trifluoroacetate, pure - Salt, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cetyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Chlorine, 10% dry gas - Element, Gas
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chlorine, 10% wet gas - Element, Gas
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chlorine, dry gas - Element, Gas
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chlorine, water solution - Oxidizer, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chlorine, wet gas - Element, Gas
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chlorine, pure - Element, Gas
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chlorine Water - Element, Gas
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chloroacetic Acid, pure - Acid, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Chlorobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chlorodifluoromethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Chloroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Chloroform, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chloromethyl Benzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Chlorosulphonic Acid, pure - Acid, Organic, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Immediate damage may occur. Not recommended for continuous use.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Chlorotoluene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Chromic Acid, 10% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chromic Acid, 20% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chromic Acid, 30% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chromic Acid, 50% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chromic Acid, 80% - Acid, Inorganic, Oxidizer
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chromic Acid, pure - Acid, Inorganic, Oxidizer
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Chromic:Surfuric Acid Mixture, 96% - Acid, Inorganic, Oxidizer
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Cinnamon Oil, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Citric Acid, 10% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Citric Acid, pure - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Copper Salts - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Copper Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cottonseed Oil, pure - Misc.
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Creosote - Hydrocarbon, Aromatic, Mixture
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Cresol Mixture - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Culture Media - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Cumene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Cyclohexane, pure - Hydrocarbon, Aliphatic, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Cyclohexanol, pure - Alcohol, Aliphatic, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Data not available.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Data not available.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Cyclohexanone, pure - Ketone, Aliphatic, Cyclic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Cyclopentane, pure - Hydrocarbon, Aliphatic, Cyclic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Decahydronaphthalene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Decalin, pure - Hydrocarbon, Aromatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Decane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Deionized Water, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Deoxycholate, pure - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

DEPC, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Detergent, Acidic - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Detergent, Alconox, pure - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Detergent, Haemo-Sol - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Detergent, NALGENE L-900 - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Dextran, pure - Misc., Sugar
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Dextran Sulfate, pure - Misc., Sugar
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Diacetone, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Diacetone Alcohol, pure - Ketone, Aliphatic, Alcohol
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Diazo Salts - Misc., Salts
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Dibasic Potassium Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Dibasic Sodium Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Dibenzopyrrole, pure - Hydrocarbon, Aromatic, Heterocyclic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Dibutyl Phthalate, pure - Ester, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dichlorobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Dichlorodifluoromethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Dichloroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dichloroethylene, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dichloromethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Diethanolamine, pure - Amine, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Diethyl Acetamide, pure - Amine, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Diethyl Benzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Diethyl Ether, pure - Ether, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Diethyl Ketone, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Diethyl Malonate, pure - Ester, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Diethylacetamide, pure - Amine, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Diethylamine, pure - Amine, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Diethylene Dioxide, pure - Ether, Cyclic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Diethylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Diethylene Glycol Monoethyl Ether, pure - Ether, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Diethylpyrocarbonate, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Dimethyl Acetamide, pure - Amine, Aliphatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dimethyl Formamide, pure - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Dimethyl Phthalate, pure - Ester, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Data not available.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dimethylacetamide, pure - Amine, Aliphatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dimethylamine, pure - Amine, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Dimethylformamide, pure - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Dimethylsulfoxide, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dioctyl Phthalate, pure - Ester, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Dioxane, pure - Ether, Cyclic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Diphenylenimine, pure - Hydrocarbon, Aromatic, Heterocyclic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Dipotassium Hydrogen Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Dipropylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Disodium Hydrogen Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Distilled Water, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

DMAC, pure - Amine, Aliphatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

DMF, pure - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

DMSO, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Dodecyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

EDTA, pure - Misc., Chelator
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Ethanol, <80% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, >80% - Alcohol, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 10% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 100% - Alcohol, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 40% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 5% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 50% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 70% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 95% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 96% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, 98% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethanolamine, pure - Amine, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ether, pure - Ether, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ethyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Ethyl Alcohol, <80% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, >80% - Alcohol, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 10% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 40% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 5% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 50% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 70% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 95% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 96% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, 98% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Ethyl Benzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Ethyl Benzoate, pure - Ester, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Ethyl Butyrate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Ethyl Chloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Ethyl Cyanoacetate, pure - Ester, Aliphatic, Cyano
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ethyl Digol, pure - Ether, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ethyl Ether, pure - Ether, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ethyl Formate, pure - Ester, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ethyl Lactate, pure - Ester, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ethylamine, pure - Amine, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ethylene Chloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ethylene Diamine Tetraacetic Acid, pure - Misc., Chelator
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Ethylene Dichloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ethylene Glycol, 30% - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Ethylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Ethylene Glycol Monobutyl Ether, pure - Ether, Aliphatic, Polyol
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ethylene Glycol Monoethyl Ether, pure - Ether, Aliphatic, Polyol
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ethylene Glycol Monoethyl Ether Acetate, pure - Ether, Aliphatic, Ester
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ethylene Glycol Monomethyl Ether, pure - Ether, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ethylene Glycol Monomethyl Ether Acetate, pure - Ether, Aliphatic, Ester
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ethylene Nitrate, pure - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Ethylene Oxide, 100% - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Ethylene Oxide, pure - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Ethylene Oxide Gas, pure - Ether, Cyclic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Ethylene Oxide Liquid, pure - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Ethylene, gas, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

EtO, 100% - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

EtO, pure - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

EtO Gas, pure - Ether, Cyclic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

EtO Liquid, pure - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Fatty Acids - saturated, pure - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Fatty Acids - unsaturated, pure - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Some effect after 7 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ferric Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ferric Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ferrous Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ferrous Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ficoll-Hypaque - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Fluoboric Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Fluorides - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Fluorine, gas - Element, gas
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... Little or no damage after 30 days of constant exposure.
TFE at 50C... Little or no damage after 30 days of constant exposure.
PFA at 50C... Little or no damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Immediate damage may occur. Not recommended for continuous use.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Fluosilicic Acid, pure - Acid, Inorganic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formaldehyde, 10% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formaldehyde, 30% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formaldehyde, 37% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formaldehyde, 40% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formaldehyde, 5% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formaldehyde, pure - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formalin, 10% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formalin, 30% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formalin, 37% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formalin, 40% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formalin, 5% - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formalin, pure - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formamide, pure - Amine, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Formic Acid, 10% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formic Acid, 100% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Formic Acid, 25% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Formic Acid, 3% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Formic Acid, 50% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Formic Acid, 85% - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Formic Acid, diluted - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Formic Acid, pure - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Freon, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Freon 12, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Freon 22, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Freon TF, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Freon TMC, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Fuel Oil, pure - Hydrocarbon, Mixture
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Furfural, pure - Aldehyde, Aliphatic, Cyclic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Furfuraldehyde, pure - Aldehyde, Aliphatic, Cyclic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Gallic Acid, pure - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Gasoline - Hydrocarbon, Mixture
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Gasoline, Refined - Hydrocarbon, Mixture
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Gasoline, Sour - Hydrocarbon, Mixture
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Glacial Acetic Acid - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Glucose, saturated - Misc., Sugar
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Glucose, pure - Misc., Sugar
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Glutaraldehyde, pure - Aldehyde, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Glutaraldehyde Disinfectant - Aldehyde, Aliphatic, Solution
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Glycerine, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Glycerol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Guanidine Hydrochloride, pure - Amine, Salt
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Guanidine Isothiocyanate, pure - Amine, Salt
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Guanidine Thiocyanate, pure - Amine, Salt
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Haemo-Sol detergent - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Helium, gas - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Heptane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Hexane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Hexanol, pure - Alcohol, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Household Bleach - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Hydrazine, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Immediate damage may occur. Not recommended for continuous use.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Hydrobromic Acid, 69% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, >6N - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, 10% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Hydrochloric Acid, 1N - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Hydrochloric Acid, 20% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, 25% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, 30% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, 35% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, 37% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, 5% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Hydrochloric Acid, 50% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, 6N - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, concentrated - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrochloric Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrocyanic Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Hydrofluoric Acid, 10% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Hydrofluoric Acid, 100% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, 35% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, 38% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, 4% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Hydrofluoric Acid, 48% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, 50% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, 53% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, 60% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, 70% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, concentrated - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluoric Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrofluosilicic Acid, pure - Acid, Inorganic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Hydroformic Acid, 100% - Acid, Organic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Hydrogen, gas - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Hydrogen Peroxide, 10% - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrogen Peroxide, 100% - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrogen Peroxide, 3% - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Hydrogen Peroxide, 30% - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrogen Peroxide, 90% - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrogen Peroxide, 94% - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrogen Peroxide, concentrated - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrogen Peroxide, pure - Peroxide, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Hydrogen Sulfide, dry gas, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Hydrogen Sulfide, wet gas, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Hydroquinone, pure - Alcohol, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Iodine Crystals - Element, Solid
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Iodine Solution - Misc.
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Iodoacetic Acid, pure - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

IPA, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

IPA, 30% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

IPA, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isobutanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isobutanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Iso-Butanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Iso-Butanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isobutyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isobutyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

iso-Butyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

iso-Butyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

iso-Octane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Data not available.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Isopropanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isopropanol, 30% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Isopropanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

iso-Propanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

iso-Propanol, 30% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

iso-Propanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isopropyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Isopropyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isopropyl Alcohol, 30% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Isopropyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

iso-Propyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

iso-Propyl Alcohol, 30% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

iso-Propyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Isopropyl Benzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Isopropyl Ether, pure - Ether Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Isopropyl Myristate, pure - Ester, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Isopropylacetone, pure - Ketone, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Jet Fuel, pure - Hydrocarbon, Mixture
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Kerosene, pure - Hydrocarbon, Mixture
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Kodak FTFR Photoresist - Misc., Photoresist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Kodak KMER Photoresist - Misc., Photoresist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Kodak KTFR Photoresist - Misc., Photoresist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Lacquer Thinner - Hydrocarbon, Mixture
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Lactic Acid, 100% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Lactic Acid, 20% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Lactic Acid, 3% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Lactic Acid, 50% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Lactic Acid, 85% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Lactic Acid, pure - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Lauryl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Lead Acetate, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Linseed Oil, pure - Misc.
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Magnesium Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Magnesium Hydroxide, saturated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Magnesium Hydroxide, unsaturated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Magnesium Hydroxide, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Magnesium Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Maleic Acid, pure - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Manganese Salts, pure - Salt, Inorganic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Mechanical Oil - Hydrocarbon, Mixture
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

MEK, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Mercaptoacetic Acid, pure - Acid, Organic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Mercuric Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Mercury - Element, Liquid
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Mercury Salts - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Mesitylene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methanol, 10% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Methanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methanol, 98% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Methanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methoxyethyl Oleate, pure - Ether, Aliphatic, Ester
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Methyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methyl Alcohol, 10% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Methyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methyl Alcohol, 98% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methyl Benzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methyl Cellosolve, pure - Ether, Aliphatic, Ester
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Methyl Cellosolve Acetate, pure - Ether, Aliphatic, Polyol
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Methyl Ethyl Ketone, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Methyl Formate, pure - Ester, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Methyl Isobutyl Ketone, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Methyl Propyl Ketone, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Methyl Salicylate, pure - Ester, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methylene Chloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Some effect after 7 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Immediate damage may occur. Not recommended for continuous use.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Methyl-t-Butyl Ether, pure - Ether, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Metrizamide - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

MIBK, pure - Ketone, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Milk - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Mineral Oil - Hydrocarbon, Mixture
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Mineral Spirits - Hydrocarbon, Mixture
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Monobasic Potassium Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Monobasic Sodium Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Monochlorobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Monochloroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Motor Oil, pure - Hydrocarbon, Mixture
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

MTBE, pure - Ether, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Muriatic Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

N,N-Diethylethanamine, pure - Amine, Alipahtic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

NALGENE L-900 detergent - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

n-Amyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

n-Amyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Naphthalene, 100% - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Naphthalene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

n-Butanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

n-Butyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

n-Butyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

n-Butyl Phthalate, pure - Ester, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

n-Decane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

n-Dodecanol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

n-Heptane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

n-Hexane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

n-Hexanol, pure - Alcohol, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Nickel Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Nickel Salts, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Nickel Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Nitric Acid, 10% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 20% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 25% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 2N - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 30% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Some effect after 7 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 50% - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 60% - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 6N - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 70% - Acid, Inorganic, Oxidizer
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, 95% - Acid, Inorganic, Oxidizer
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, concentrated - Acid, Inorganic, Oxidizer
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, fuming - Acid, Inorganic, Oxidizer
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitric Acid, pure - Acid, Inorganic, Oxidizer
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitrobenzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nitrogen, gas - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Nitromethane, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

n-Octane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

n-Pentane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

n-Pentanol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

n-Propane, liquid - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

n-Propane, gas, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

n-Propanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

n-Propyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Nycodenz - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... No damage after 30 days of constant exposure.

o-Dichlorobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Oil of Wintergreen, pure - Ester, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Oil, Cedarwood, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Oil, Cinnamon, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Oil, Cottonseed, pure - Misc.
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Oil, Linseed, pure - Misc.
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Oil, Mineral - Hydrocarbon, Mixture
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Oil, Paraffin, pure - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Oil, Peanut, pure - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Oil, Petroleum - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Oil, Pine, pure - Misc.
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Oil, Sesame, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Oil, Silicone, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Oil, Vegetable - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Oil, Wintergreen, pure - Ester, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Oleic Acid, pure - Acid, Organic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Oleum, pure - Acid, Inorganic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Orange Oil, pure - Misc.
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Oxalic Acid, <50% - Acid, Organic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Oxalic Acid, 10% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Oxalic Acid, 50% - Acid, Organic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Oxalic Acid, pure - Acid, Organic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Oxygen, gas, pure - Element, Gas
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ozone, 10ppm in Water - Oxidizer, Inorganic, Solution
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Ozone, pure - Oxidizer, Inorganic, Gas
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Palmitic Acid, pure - Acid, Organic
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Paraffin - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Paraffin oil - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Paraffin, White - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Paraldehyde - Ketone, Aliphatic, Cyclic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

p-Chloroacetophenone, pure - Ketone, Aromatic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

p-Dichlorobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Peanut oil, pure - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Pentane, pure - Hydrocarbon, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Pentanol, pure - Alcohol, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Peracetic Acid, 0.2% - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Perchloric Acid, 10% - Acid, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Perchloric Acid, 25% - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Perchloric Acid, 60% - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... Some effect after 7 days of constant exposure.
TFE at 20C... Little or no damage after 30 days of constant exposure.
PFA at 20C... Little or no damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... Immediate damage may occur. Not recommended for continuous use.
TFE at 50C... Some effect after 7 days of constant exposure.
PFA at 50C... Some effect after 7 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Perchloric Acid, 70% - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... Immediate damage may occur. Not recommended for continuous use.
TFE at 20C... Little or no damage after 30 days of constant exposure.
PFA at 20C... Little or no damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... Immediate damage may occur. Not recommended for continuous use.
TFE at 50C... Some effect after 7 days of constant exposure.
PFA at 50C... Some effect after 7 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Perchloric Acid, concentrated - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... Immediate damage may occur. Not recommended for continuous use.
TFE at 20C... Little or no damage after 30 days of constant exposure.
PFA at 20C... Little or no damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... Immediate damage may occur. Not recommended for continuous use.
TFE at 50C... Some effect after 7 days of constant exposure.
PFA at 50C... Some effect after 7 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Perchloric Acid, pure - Acid, Inorganic, Oxidizer
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... Immediate damage may occur. Not recommended for continuous use.
TFE at 20C... Little or no damage after 30 days of constant exposure.
PFA at 20C... Little or no damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... Immediate damage may occur. Not recommended for continuous use.
TFE at 50C... Some effect after 7 days of constant exposure.
PFA at 50C... Some effect after 7 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Perchloroethylene, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Percoll - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Petrol - Hydrocarbon, Mixture
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Petroleum - Hydrocarbon, Mixture
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Petroleum Ether, pure - Ether, Mixture
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Petroleum Oil - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Phenol, 10% - Alcohol, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, 10% Aqueous - Alcohol, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, 100% - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, 5% - Alcohol, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, 50% - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, 92% - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, liquid - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, pure - Alcohol, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenol, Crystals, pure - Alcohol, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Phenylethanol, pure - Alcohol, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Phenylethyl Alcohol, pure - Alcohol, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Phosphoric Acid, 10% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Phosphoric Acid, 25% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Phosphoric Acid, 30% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Phosphoric Acid, 5% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Phosphoric Acid, 50% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Phosphoric Acid, 85% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Phosphoric Acid, 88% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Phosphoric Acid, 95% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Phosphoric Acid, concentrated - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Phosphoric Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Phosphorus Trichloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Photographic Hypo - Salt, Inorganic, Reducer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Photoresists - Misc., Photoreist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Picric Acid, pure - Acid, Organic, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Pine Oil, pure - Misc.
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Polyethylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Polyethylene Glycol 1000, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Polyethylene Glycol 300, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Potassium Acetate, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Bromide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Carbonate, saturated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Carbonate, unsaturated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Carbonate, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Chlorate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Chloride, saturated - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Chloride, unsaturated - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Cyanide, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Dihydrogen Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Potassium Hydroxide, 1% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 10% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 15% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 1N - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 30% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 32% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 3N - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 45% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 5% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 50% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, 6N - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, concentrated - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Potassium Hydroxide, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... No damage after 30 days of constant exposure.

Potassium Iodide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Permanganate, pure - Salt, Inorganic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Potassium Phosphate Dibasic, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Potassium Phosphate Monobasic, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Potassium Phosphate Tribasic, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Potassium Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Propane, gas - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Propane, liquid - Hydrocarbon, Aliphatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Propanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Proprionic Acid, pure - Acid, Organic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Propyl Acetate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Propyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Propylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Propylene Glycol Acetate, pure - Ester, Aliphatic, Polyol
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Propylene Oxide, pure - Ether, Cyclic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Prussic Acid, Hydrogen, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Pseudocumene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Pyridine, 5% - Amine, Heterocyclic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Some effect after 7 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Pyridine, 50% - Amine, Heterocyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Pyridine, pure - Amine, Heterocyclic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Quinone, pure - Ketone, Aliphatic, Cyclic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Resorcinol, 5% - Alcohol, Aromatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Resorcinol, saturated - Alcohol, Aromatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Resorcinol, pure - Alcohol, Aromatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Rubidium Bromide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Rubidium Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sal Ammoniac, saturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sal Ammoniac, unsaturated - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sal Ammoniac, pure - Salt, Inorganic, Amine
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Salicylaldehyde, pure - Ester, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Salicylic Acid, saturated - Acid, Organic, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Salicylic Acid, powder, 100% - Acid, Organic, Aromatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

SDS, pure - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sea Water, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

sec-Butanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

sec-Butanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

sec-Butyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

sec-Butyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sera - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sesame Oil, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Shipley AZ-111 Photoresist - Misc., Photoresist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Shipley AZ-1350 Photoresist - Misc., Photoresist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Shipley AZ-340 Photoresist - Misc., Photoresist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Silica Gel, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Silicic Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Silicone Oil, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Silver Acetate, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Silver Cyanide, pure - Salt, Organic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Silver Nitrate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Skydrol 500 - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Skydrol LD4 - Misc.
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Acetate, saturated - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Acetate, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Bicarbonate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Bisulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Bisulfite, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... No damage after 30 days of constant exposure.

Sodium Borate, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Bromide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Carbonate, 2% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Carbonate, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Sodium Chlorate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Chloride, 10% - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Sodium Chloride, 36% - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Sodium Chloride, saturated - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Sodium Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Sodium Cyanide, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Dichromate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Dihydrogen Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Sodium Dodecyl Sulfate, pure - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Hydroxide, <1% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 1% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 10% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 1N - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 32% - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 3N - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 5% - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 50% - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 52% - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, 6N - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, concentrated - Base/Caustic, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hydroxide, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... No damage after 30 days of constant exposure.

Sodium Hypochlorite, 15% - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Hypochlorite, 5% - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Hypochlorite, pure - Base/Caustic, Oxidizer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sodium Iodide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Lauryl Sulfate, pure - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Metaborate, pure - Salt, Inorganic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Nitrate, 10% - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Nitrate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Perborate, pure - Salt, Inorganic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Peroxide, pure - Peroxide, Inorganic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Sodium Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Phosphate Dibasic, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Sodium Phosphate Monobasic, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Sodium Silicate, pure - Base/Caustic, Inorganic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Sulfide, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Sodium Sulfite, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Tetraborate, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sodium Thiosulfate, pure - Salt, Inorganic, Reducer
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Solution 555, 20% - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Stearic Acid, pure - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Stoddard Solvents, pure - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Sucrose, pure - Misc., Sugar
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Sucrose, Alkaline, pure - Misc., Sugar, Base/Caustic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Sulfosalicylic Acid, pure - Acid, Organic, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Sulfur Chloride, pure - Acid, Inorganic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Sulfur Dioxide, dry gas - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sulfur Dioxide, liquid - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Sulfur Dioxide, wet gas - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Sulfur Dioxide, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Sulfur Salts, pure - Salt, Inorganic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Some effect after 7 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Sulfuric Acid, 10% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 100% - Acid, Inorganic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 20% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 25% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 2N - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 30% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 50% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 6% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 60% - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 6N - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 75% - Acid, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 96% - Acid, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, 98% - Acid, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, concentrated - Acid, Inorganic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, fuming - Acid, Inorganic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuric Acid, pure - Acid, Inorganic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulfuryl Chloride, pure - Misc.
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... Little or no damage after 30 days of constant exposure.
TFE at 20C... Little or no damage after 30 days of constant exposure.
PFA at 20C... Little or no damage after 30 days of constant exposure.
ECTFE at 20C... Some effect after 7 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... Some effect after 7 days of constant exposure.
TFE at 50C... Some effect after 7 days of constant exposure.
PFA at 50C... Some effect after 7 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Sulphurous Acid, pure - Acid, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

sym-Trimethylbenzene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Little or no damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Tannic Acid, pure - Acid, Organic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Tap Water - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Tartaric Acid, pure - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Some effect after 7 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

TCA, 10% - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

TCA, 100% - Acid, Organic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

TCA, 25% - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

TCA, pure - Acid, Organic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

tert-Butanol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

tert-Butanol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

tert-Butyl Alcohol, 100% - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

tert-Butyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Tetrachloroethylene, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Tetrahydrofuran, pure - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Tetrahydronaphthalene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Tetralin, pure - Hydrocarbon, Aromatic
LDPE at 20C... Data not available.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

TFA, 100% - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

TFA, 20% - Acid, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

TFA, 4% - Acid, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

TFA, 48% - Acid, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

TFA, pure - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

THF, pure - Ether, Cyclic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Thioglycollic Acid, pure - Acid, Organic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Thionyl Chloride, pure - Salt, Inorganic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Tincture of Iodine - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Data not available.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Toluene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Toluol, pure - Hydrocarbon, Aromatic
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Transformer Oil, pure - Misc.
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Some effect after 7 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Tribasic Potassium Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Tributyl Citrate, pure - Ester, Aliphatic
LDPE at 20C... Little or no damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Little or no damage after 30 days of constant exposure.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Some effect after 7 days of constant exposure.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Some effect after 7 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Trichloroacetic Acid, 10% - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Trichloroacetic Acid, 100% - Acid, Organic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Trichloroacetic Acid, 25% - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Trichloroacetic Acid, pure - Acid, Organic, Halogenated
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Some effect after 7 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Little or no damage after 30 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Trichlorobenzene, pure - Hydrocarbon, Aromatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Trichloroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Immediate damage may occur. Not recommended for continuous use.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Trichloroethylene, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Trichlorofluoromethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Trichlorotrifluoroethane, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Some effect after 7 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Tricresyl Phosphate, pure - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Immediate damage may occur. Not recommended for continuous use.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Immediate damage may occur. Not recommended for continuous use.
PMX at 50C... Data not available.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Triethanolamine, pure - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Immediate damage may occur. Not recommended for continuous use.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Triethylamine, pure - Amine, Aliphatic
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Trimethylamine, pure - Amine, Alipahtic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Data not available.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Triethylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Trifluoroacetic Acid, 100% - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Trifluoroacetic Acid, 20% - Acid, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

Trifluoroacetic Acid, 4% - Acid, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Some effect after 7 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Some effect after 7 days of constant exposure.

Trifluoroacetic Acid, 48% - Acid, Organic, Halogenated
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Trifluoroacetic Acid, pure - Acid, Organic, Halogenated
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Immediate damage may occur. Not recommended for continuous use.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Immediate damage may occur. Not recommended for continuous use.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Little or no damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Tripotassium Phosphate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Tripropylene Glycol, pure - Alcohol, Aliphatic, Polyol
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Tris Buffer Solution, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Little or no damage after 30 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... No damage after 30 days of constant exposure.

Trisodium Phosphate, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Triton X-100, pure - Detergent
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... Little or no damage after 30 days of constant exposure.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

TSP, pure - Base/Caustic, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Turpentine - Hydrocarbon, Mixture
LDPE at 20C... Some effect after 7 days of constant exposure.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Some effect after 7 days of constant exposure.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Little or no damage after 30 days of constant exposure.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Some effect after 7 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

Undecyl Alcohol, pure - Alcohol, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Some effect after 7 days of constant exposure.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Little or no damage after 30 days of constant exposure.
PPCO at 50C... Little or no damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Little or no damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Urea, pure - Amine, Aliphatic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... Little or no damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Some effect after 7 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... Little or no damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Little or no damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Urine - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Little or no damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... Little or no damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Vegetable Oil, pure - Misc.
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Some effect after 7 days of constant exposure.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Vinegar, pure - Acid, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Some effect after 7 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Immediate damage may occur. Not recommended for continuous use.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Little or no damage after 30 days of constant exposure.
RPVC at 50C... Some effect after 7 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... Little or no damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Vinylidene Chloride, pure - Hydrocarbon, Aliphatic, Halogenated
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Immediate damage may occur. Not recommended for continuous use.
PMP at 20C... Immediate damage may occur. Not recommended for continuous use.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Little or no damage after 30 days of constant exposure.
ETFE at 20C... Little or no damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Immediate damage may occur. Not recommended for continuous use.
TMX at 20C... Data not available.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Some effect after 7 days of constant exposure.
ETFE at 50C... Some effect after 7 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Water Glass, pure - Base/Caustic, Inorganic
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... Little or no damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... Data not available.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Some effect after 7 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... Data not available.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Water, Deionized, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Water, Distilled, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Little or no damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Water, Sea, pure - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Water, Tap - Misc.
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... No damage after 30 days of constant exposure.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... No damage after 30 days of constant exposure.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Some effect after 7 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Little or no damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Waycoat 59 Photoresist - Misc., Photoresist
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Data not available.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... Data not available.
ETFE at 20C... Data not available.
PC at 20C... Data not available.
RPVC at 20C... Data not available.
PVCT at 20C... Data not available.
PSF at 20C... Data not available.
PS at 20C... Data not available.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Data not available.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Data not available.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... Data not available.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... Data not available.
PVCT at 50C... Data not available.
PSF at 50C... Data not available.
PS at 50C... Data not available.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Data not available.
TMX at 50C... Data not available.

White Paraffin, pure - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... Little or no damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... Little or no damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... Data not available.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... Data not available.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Little or no damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Little or no damage after 30 days of constant exposure.
PP at 50C... Some effect after 7 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... Some effect after 7 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Data not available.
PC at 50C... Data not available.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Data not available.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Some effect after 7 days of constant exposure.
TMX at 50C... Data not available.

White Spirits - Hydrocarbon, Mixture
LDPE at 20C... Data not available.
HDPE at 20C... Data not available.
PP at 20C... Data not available.
PPCO at 20C... Data not available.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... Data not available.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... Data not available.
HDPE at 50C... Data not available.
PP at 50C... Data not available.
PPCO at 50C... Data not available.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... Little or no damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... Data not available.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Data not available.

Xylene, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Xylol, pure - Hydrocarbon, Aromatic
LDPE at 20C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 20C... Some effect after 7 days of constant exposure.
PP at 20C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 20C... Some effect after 7 days of constant exposure.
PMP at 20C... Some effect after 7 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 20C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 20C... Immediate damage may occur. Not recommended for continuous use.
PSF at 20C... Immediate damage may occur. Not recommended for continuous use.
PS at 20C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... Some effect after 7 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
HDPE at 50C... Immediate damage may occur. Not recommended for continuous use.
PP at 50C... Immediate damage may occur. Not recommended for continuous use.
PPCO at 50C... Immediate damage may occur. Not recommended for continuous use.
PMP at 50C... Immediate damage may occur. Not recommended for continuous use.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... Little or no damage after 30 days of constant exposure.
PC at 50C... Immediate damage may occur. Not recommended for continuous use.
RPVC at 50C... Immediate damage may occur. Not recommended for continuous use.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... Immediate damage may occur. Not recommended for continuous use.
PS at 50C... Immediate damage may occur. Not recommended for continuous use.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... Immediate damage may occur. Not recommended for continuous use.
TMX at 50C... Immediate damage may occur. Not recommended for continuous use.

Zephiran Chloride, 1% - Misc., Disinfectant
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Zephiran Chloride, 7% - Misc., Disinfectant
LDPE at 20C... Data not available.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... Data not available.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Data not available.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... Data not available.
PVCT at 20C... No damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Little or no damage after 30 days of constant exposure.
LDPE at 50C... Data not available.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... Data not available.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Data not available.
PVCT at 50C... No damage after 30 days of constant exposure.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Zinc Chloride, 10% - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Immediate damage may occur. Not recommended for continuous use.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Zinc Chloride, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Some effect after 7 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Little or no damage after 30 days of constant exposure.

Zinc Stearate, pure - Salt, Organic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... No damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... No damage after 30 days of constant exposure.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... Little or no damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Zinc Sulfate, 10% - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Some effect after 7 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... No damage after 30 days of constant exposure.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Immediate damage may occur. Not recommended for continuous use.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.

Zinc Sulfate, pure - Salt, Inorganic
LDPE at 20C... No damage after 30 days of constant exposure.
HDPE at 20C... No damage after 30 days of constant exposure.
PP at 20C... No damage after 30 days of constant exposure.
PPCO at 20C... No damage after 30 days of constant exposure.
PMP at 20C... No damage after 30 days of constant exposure.
PETG at 20C... Data not available.
NYL at 20C... Little or no damage after 30 days of constant exposure.
FEP at 20C... No damage after 30 days of constant exposure.
TFE at 20C... No damage after 30 days of constant exposure.
PFA at 20C... No damage after 30 days of constant exposure.
ECTFE at 20C... No damage after 30 days of constant exposure.
ETFE at 20C... No damage after 30 days of constant exposure.
PC at 20C... No damage after 30 days of constant exposure.
RPVC at 20C... No damage after 30 days of constant exposure.
PVCT at 20C... Little or no damage after 30 days of constant exposure.
PSF at 20C... No damage after 30 days of constant exposure.
PS at 20C... No damage after 30 days of constant exposure.
PVDF at 20C... No damage after 30 days of constant exposure.
PMX at 20C... No damage after 30 days of constant exposure.
TMX at 20C... Data not available.
LDPE at 50C... No damage after 30 days of constant exposure.
HDPE at 50C... No damage after 30 days of constant exposure.
PP at 50C... No damage after 30 days of constant exposure.
PPCO at 50C... No damage after 30 days of constant exposure.
PMP at 50C... No damage after 30 days of constant exposure.
PETG at 50C... Data not available.
NYL at 50C... Data not available.
FEP at 50C... No damage after 30 days of constant exposure.
TFE at 50C... No damage after 30 days of constant exposure.
PFA at 50C... No damage after 30 days of constant exposure.
ECTFE at 50C... No damage after 30 days of constant exposure.
ETFE at 50C... No damage after 30 days of constant exposure.
PC at 50C... No damage after 30 days of constant exposure.
RPVC at 50C... No damage after 30 days of constant exposure.
PVCT at 50C... Immediate damage may occur. Not recommended for continuous use.
PSF at 50C... No damage after 30 days of constant exposure.
PS at 50C... No damage after 30 days of constant exposure.
PVDF at 50C... No damage after 30 days of constant exposure.
PMX at 50C... No damage after 30 days of constant exposure.
TMX at 50C... Data not available.